Mechanical, thermal and colorimetric properties of LLDPE coloured with a blue nanopigment and conventional blue pigments

Purpose – This research deals with a new kind of nanopigment, obtained from the combination of organic dyes and layered nanoclays, that the authors call nanoclay-colorant pigment (NCP). Whilst they have already been employed in inks and coatings, to date these nanopigments have not been used as pigments for polymers. The existing lack of knowledge surrounding them must be redressed in order to bridge the gap between current academic studies and commercial exploitation. Therefore, the main purpose of this paper is to examine the hitherto unknown aspects of the NCP, which relate specifically to their applicability as a new type of colorant for polymers. Design/methodology/approach – A blue NCP has been prepared at the laboratory according to the patented method of synthesis (patent WO0104216), using methylene blue and montmorillonite nanoclay. It has then been applied to a thermoplastic polymer (linear low-density polyethylene – LLDPE) to obtain a coloured sample. Furthermore, samples with the same polymer but using conventional blue colorants have been prepared under the same processing conditions. The mechanical, thermal and colorimetric properties of these materials have been compared. Findings – The thermal stability of the sample coloured with NCP is reduced to some extent, while the mechanical strength is slightly increased. Moreover, this sample has better colour performance than the conventionally pigmented samples. Originality/value – In this paper, a blue NCP has been synthesised and successfully employed with polyethylene and the obtained sample shows better colour performance than polyethylene with conventional pigments.

Novel Ti/Ta2O5-SnO2 electrodes for water electrolysis and electrocatalytic oxidation of organics

Mixed metal oxide (MMO) electrodes have been applied to different technologies including chlorine production, organic compounds oxidation, water electrolysis, electroplating, etc. due to their catalytic, optical and electronic properties. Most of the existing MMO electrodes contain either toxic metals or precious metals of the platinum group. The aim of this study was to develop environmentally friendly and cost-effective MMO electrodes for water and organic compounds oxidation. Ti/Ta2O5-SnO2 electrodes of different nominal composition were prepared, and electrochemically and physically characterized. For water oxidation, Ti/SnO2 electrode with 5 at.% of Ta produced the highest electroactivity. Ti/SnO2 electrode with 7.5 at.% of Ta showed the best performance for the oxidation of methylene blue (MB). The electrocatalytic activity of the Ti/Ta2O5-SnO2 electrodes increased with the number of active layers. The maximum current of water oxidation reached 3.5 mA at 2.5 V when the electrode was covered with ten layers of Ta2O5. In case of the oxidation of 0.1 mM MB, eight and ten active layers of Ta2O5 significantly increased the electrode activity. The prepared electrodes have been found applicable for both water electrolysis and organic compounds oxidation.

Linear low-density polyethylene colored with a nanoclay-based pigment: Morphology and mechanical, thermal, and colorimetric properties

In this study, a novel kind of hybrid pigment based on nanoclays and dyes was synthesized and characterized. These nanoclay-based pigments (NCPs) were prepared at the laboratory with sodium montmorillonite nanoclay (NC) and methylene blue (MB). The cation-exchange capacity of NC exchanged with MB was varied to obtain a wide color gamut. The synthesized nanopigments were thoroughly characterized. The NCPs were melt-mixed with linear low-density polyethylene (PE) with an internal mixer. Furthermore, samples with conventional colorants were prepared in the same way. Then, the properties (mechanical, thermal, and colorimetric) of the mixtures were assessed. The PE–NCP samples developed better color properties than those containing conventional colorants and used as references, and their other properties were maintained or improved, even at lower contents of dye compared to that with the conventional colorants.

Characterisation of montmorillonites simultaneously modified with an organic dye and an ammonium salt at different dye/salt ratios. Properties of these modified montmorillonites EVA nanocomposites

In this work, a sodium montmorillonite (Na+-Mt) was modified with two molecules simultaneously, an organic dye, methylene blue (MB), and ethyl hexadecyl dimethyl ammonium (EHDDMA). The synthesised organo-montmorillonites (OMt) combining different proportions of the two molecules were thoroughly characterised and mixed with ethylene vinyl acetate copolymer (EVA) in order to check the ability of these OMt as pigments and reinforcing additives. The synthesised OMt combining both surfactants, MB and EHDDMA, present higher interlayer distances than those with only MB, which were employed in previous works as nanopigments. When these OMt were incorporated in the EVA matrix, the obtained clay polymer nanocomposites (CPN) showed a high exfoliation degree of the OMt in the polymer, in such a way that at 80% of the cationic exchange capacity (CEC) of the Mt exchanged with EHDDMA, most of the OMt was exfoliated. Moreover, all the obtained CPN showed an increase in the Young's Moduli compared to the EVA reference, and especially those containing higher amounts of MB. The thermal stability of the CPN also increases with the MB content, compared to other CPN including conventional surfactants. The hiding power and colouring power achieved in the CPN are higher even with a much lower load of MB when EHDDMA is exchanged in the Mt.